Product Description

I. Basic performance and application
T**3 antifoaming agent can clean the powder of the air hole which is caused by powder containing water and iron, aluminum or other castings containing water and have good effect on increasing hardness and resisting scratch and adhesion, specially for the large area of foaming on iron casting, aluminum casting or other heavier workpieces. It is applicable to various powders and enjoys more effect as transparent powder, similar with BYK**1.
 
II. Technical indexes
Appearance:                                                               white flowable powder
Melting point:                                                             **5~**0℃
Volatile content:                                                         ≤0.3%
 
III. Basic ingredients of powder coating (full gloss, white powder) (dose: 0.5~1% inner extruding)
Name                                                                           Weight
Epoxy resin (E**2)                                                       **0
Polyester resin (5: 5)                                                   **0
Titanium pigment (rutile)                                              **0
Precipitated barium sulfate                                           **0
T*8 pure leveling agent                                               *0
T**1 luster-enhancing agent                                       *0
T**3 antifoaming agent                                               5
T**2 high light wax                                                      5
 
IV. Coating manufacturing technology:
Extruder: double screw extruder
Extruder prezone temperature:                                  **5º
Extruder postzone temperature:                                **0º
Extruder speed:                                                         *0HZ
 
V. Baking temperature: **0º/*5min or **0º/*0min
Basic performance of coating film: film thickness of *0~*0μm
Impact strength (positive and negative):                      *0kg/cm passed
Pencil hardness:                                                        ≥2H
glossiness (*0º angle):                                               ≥*0º
Bending (Φ2um):      passed